Shofu Hi-Dense Xp Eco Pack is a silver re-inforced glass ionomer cement (miracle mix) which is ideally used for restorations in posterior teeth. Created for permanent restoration of posterior deciduous teeth, non-stress bearing permanent teeth, core build-up and repair of amalgam restorations.

INDICATIONS:
For Permanent restoration of posterior deciduous teeth
For Non-stress bearing permanent teeth
For Core build-up and repair of amalgam restorations.

Features:
Contains spherical silver-tin alloy particles in a specially formulated glass ionomer powder for better performance with exceptional handling and physical properties even under humid conditions.
High compressive strength prevents cuspal flexure under large composite restorations
Exhibits excellent adhesion to tooth structure, pins and amalgam.
Silver powder is premixed for easy homogeneous mixing
Packable and condensable like amalgam without mercury. Radiopaque, excellent fluoride release and recharge with high resistance to erosion.

TECHNICAL SPECIFICATIONS:
Powder / Liquid Ratio 4.5 / 1.0
Working Time 23 degrees C 1 min 45 secs to 2 minutes 30 seconds (from start of mixing)
Clinical Setting Time 37 degrees C 3 mins to 3mins 30 secs (from end of mixing)

Usage Directions:
Preparation: Begin by preparing the tooth as needed for the specific restoration or repair procedure, such as removing decayed or damaged tissue and shaping the tooth structure.
Mixing: Open the Eco Pack container and dispense the powder and liquid components onto a mixing pad. Use a spatula to mix the two components together until a homogenous mixture is achieved. Application: Using an appropriate dental instrument, apply the mixed material to the prepared tooth surface, ensuring adequate coverage and adaptation to the tooth structure. For posterior teeth, it is recommended to apply the material in increments to avoid excess bulk and ensure proper curing.
Finishing and Polishing: Once the material has set, use appropriate finishing and polishing instruments to shape and contour the restoration to achieve the desired form and function.